Complete Experimental Process of Piezoceramics
Complete Experimental Process of Piezoceramics
Complete Experimental Process of Piezoceramics
1. Experimental Purpose
This experiment takes PZT-based or lead-free piezoceramic systems as research objects to complete the whole process from powder preparation, molding and sintering to polarization treatment. A fully automatic tablet press is used to prepare high-density ceramic green bodies, and an 8-channel high-voltage polarization device is adopted for parallel polarization of multiple samples. The influence laws of molding pressure, polarization electric field, polarization temperature, polarization time and other process parameters on the microstructure and electrical properties of piezoceramics are systematically studied, providing experimental basis for the optimized preparation of high-performance piezoceramic materials.
2. Experimental Materials and Equipment
2.1 Experimental Materials
Piezoceramic powder (pre-synthesized PZT-based or KNN-based lead-free system)
Polyvinyl alcohol (PVA) binder (concentration 5–8 wt%)
Anhydrous ethanol (analytical grade)
Silver paste (for electrode preparation)
Methyl silicone oil (polarization medium)
2.2 Experimental Equipment
Fully automatic tablet press (equipped with molds of Φ10mm/Φ15mm/Φ20mm and other specifications)
PZT-JH30/8 8-channel high-voltage polarization device
Box-type resistance furnace (for sintering)
High-temperature oven (for binder removal)
Ultrasonic cleaner
Screen printing station or silver coating pen
Electronic analytical balance (accuracy 0.1mg)
3. Experimental Steps
Stage 1: Powder Preparation and Granulation (Pre-process)
Step 1: Pre-sintered Powder Preparation
Weigh Pb?O?, ZrO?, TiO? (or raw materials such as K?CO?, Na?CO?, Nb?O? for lead-free systems) according to stoichiometric ratio, add anhydrous ethanol for planetary ball milling for 24 hours. Dry the slurry in an 80℃ oven for 12 hours, sieve through a 60-mesh sieve, then put into an alumina crucible for pre-sintering at 850–950℃ for 2–4 hours to complete perovskite phase synthesis.
免責聲明
- 凡本網注明“來源：化工儀器網”的所有作品，均為浙江興旺寶明通網絡有限公司-化工儀器網合法擁有版權或有權使用的作品，未經本網授權不得轉載、摘編或利用其它方式使用上述作品。已經本網授權使用作品的，應在授權范圍內使用，并注明“來源：化工儀器網”。違反上述聲明者，本網將追究其相關法律責任。
- 本網轉載并注明自其他來源（非化工儀器網）的作品，目的在于傳遞更多信息，并不代表本網贊同其觀點和對其真實性負責，不承擔此類作品侵權行為的直接責任及連帶責任。其他媒體、網站或個人從本網轉載時，必須保留本網注明的作品第一來源，并自負版權等法律責任。
- 如涉及作品內容、版權等問題，請在作品發表之日起一周內與本網聯系，否則視為放棄相關權利。
采購中心